LEXAN ML6413 resin is an impact modified, flame retardant polycarbonate grade with Br- & Cl-free FR systems. It features improved light shielding capability with balanced properties suitable for various applications.
阻燃,改性塑料
LEXAN ML6413物性表
Property
TYPICAL PROPERTIES (1)
MECHANICAL
Value
Unit
Standard
Tensile Stress, yld, Type I, 50 mm/min
590
kgf/cm2
ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min
560
kgf/cm2
ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min
5
%
ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min
100
%
ASTM D 638
Tensile Modulus, 5 mm/min
25400
kgf/cm2
ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
860
kgf/cm2
ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span
22900
kgf/cm2
ASTM D 790
Tensile Stress, yield, 50 mm/min
62
MPa
ISO 527
Tensile Stress, break, 50 mm/min
58
MPa
ISO 527
Tensile Strain, yield, 50 mm/min
5
%
ISO 527
Tensile Strain, break, 50 mm/min
100
%
ISO 527
Tensile Modulus, 1 mm/min
2350
MPa
ISO 527
Flexural Stress, yield, 2 mm/min
90
MPa
ISO 178
Flexural Modulus, 2 mm/min
2350
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact, notched, 23°C
80
cm-kgf/cm
ASTM D 256
Izod Impact, notched, -30°C
15
cm-kgf/cm
ASTM D 256
Instrumented Impact Total Energy, 23°C
734
cm-kgf
ASTM D 3763
Izod Impact, notched 80*10*3 +23°C
60
kJ/m2
ISO 180/1A
Izod Impact, notched 80*10*3 -30°C
15
kJ/m2
ISO 180/1A
THERMAL
Value
Unit
Standard
Vicat Softening Temp, Rate B/50
134
°C
ASTM D 1525
HDT, 1.82 MPa, 6.4 mm, unannealed
118
°C
ASTM D 648
CTE, -40°C to 40°C, flow
7.7E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, xflow
5.9E-05
1/°C
ASTM E 831
CTE, -40°C to 40°C, flow
7.E-05
1/°C
ISO 11359-2
CTE, -40°C to 40°C, xflow
7.E-05
1/°C
ISO 11359-2
Vicat Softening Temp, Rate B/50
134
°C
ISO 306
Vicat Softening Temp, Rate B/120
135
°C
ISO 306
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
125
°C
ISO 75/Be
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
115
°C
ISO 75/Ae
Relative Temp Index, Elec
100
°C
UL 746B
Relative Temp Index, Mech w/impact
100
°C
UL 746B
Relative Temp Index, Mech w/o impact
100
°C
UL 746B
PHYSICAL
Value
Unit
Standard
Specific Gravity
1.2
-
ASTM D 792
Mold Shrinkage, flow, 3.2 mm (5)
0.4 - 0.8
%
SABIC Method
Melt Flow Rate, 260°C/5.0 kgf
24
g/10 min
ASTM D 1238
Density
1.2
g/cm3
ISO 1183
Water Absorption, (23°C/sat)
0.3
%
ISO 62
Moisture Absorption (23°C / 50% RH)
0.1
%
ISO 62
Melt Volume Rate, MVR at 260°C/5.0 kg
20
cm3/10 min
ISO 1133
ELECTRICAL
Value
Unit
Standard
Volume Resistivity
>1.E+15
Ohm-cm
ASTM D 257
Hot Wire Ignition {PLC)
3
PLC Code
UL 746A
Comparative Tracking Index (UL) {PLC}
2
PLC Code
UL 746A
FLAME CHARACTERISTICS
Value
Unit
Standard
UL Recognized, 94V-0 Flame Class Rating (3)
1.6
mm
UL 94
UL Recognized, 94-5VA Rating (3)
3
mm
UL 94
UL Recognized, 94-5VB Rating (3)
2
mm
UL 94
Glow Wire Flammability Index 960°C, passes at
1.6
mm
IEC 60695-2-12
Glow Wire Ignitability Temperature, 2.0 mm
800
°C
IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm
800
°C
IEC 60695-2-13
Source GMD, last updated:2006/10/19
Processing
Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 90 - 100 | °C |
Drying Time | 2 - 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 270 - 300 | °C |
Nozzle Temperature | 250 - 290 | °C |
Front - Zone 3 Temperature | 260 - 300 | °C |
Middle - Zone 2 Temperature | 250 - 290 | °C |
Rear - Zone 1 Temperature | 230 - 260 | °C |
Hopper Temperature | 60 - 80 | °C |
Mold Temperature | 60 - 90 |
°C |
3412R
3412R GY6B428
3412R-131
3412R-73223
3412R-739
3412R-739(2)
3412R-75301
3413
3413R
3413R GY
3413R-131
3413R-739
3414-73253
3414R-131
3414R-739
4019
4351
4351R
4501-110001
4504-11003
4504R-11003
451E-1001
4610
4631-10001
4701-110001
4701-7000
4701R
4701R GY7C050
4701R-110001
4701R-11001
4701R-701
500
500-7040
500-7388
500-739
500ECR BK6A237
500ECR BL6A237L
500ECR GY8002L
500ECR GY90200
500ECR WH
500ECR WH9A459L
500ECR-131/739
500ECR-739L BK
500ECR-BK
500R
500R-131
500R-731
500R-73234
500R-739
500R-73966
500R-13021
500R-GY